Aryldiamine compound and organic electroluminescent element

ABSTRACT

An aryldiamine compound represented by formula (1) and an organic electroluminescent device including a pair of electrodes and at least one organic layer disposed therebetween wherein the at least one organic layer contains the aryldiamine compound. The aryldiamine compound is excellent in hole transporting properties, hole injection properties, electron blocking properties, stability in thin film form, and heat resistance. The organic electroluminescent device achieves high emission efficiency and power efficiency, drives at a low voltage, and, in particular, has a long life.

TECHNICAL FIELD

This invention relates to a compound suited for use in an organic electroluminescent device (hereinafter referred to as an organic EL device) and an organic EL device. More particularly, it relates to a specific aryldiamine compound and an organic EL device using the compound.

BACKGROUND ART

An organic EL device is self-luminescent, so that the organic EL device enables brighter, more visible, and clearer image display than liquid crystal devices and has therefore been studied extensively.

C. W. Tang, et al. of Eastman Kodak developed a stacked device having a plurality of materials each performing its own role in 1987 and put an organic EL device using organic materials to practical use. An organic EL device is fabricated by stacking a fluorescent substance capable of transporting electrons and an organic substance capable of transporting holes. The opposite charges are injected to the emitting layer of the fluorescent substance to emit light, whereby a luminance as high as 1000 cd/m² or even higher is obtained at a voltage of 10 V or lower (see patent literatures 1 and 2 below).

A number of improvements have so far been added to existing organic EL devices with a view to practical use. For example, the roles of the stacked layers are further divided such that the EL device is composed of a substrate, an anode, a hole injection layer, a hole transport layer, an emitting layer, an electron transport layer, an electron injection layer, and a cathode stacked in that order. Such a structure has been achieving high efficiency and durability.

With the view of further improvement of emission efficiency, use of triplet excitons has been attempted, and studies have been directed to use of phosphorescent compounds. Devices utilizing emission by thermally activated delayed fluorescence (TADF) have also been under development. Adachi, et al. of Kyusyu University achieved an external quantum efficiency of 5.3% by their device comprising a TADF material in 2011.

An emitting layer is generally formed by doping a charge transport compound called a host material with a fluorescent compound, a phosphorescent compound, or a delayed fluorescence emitter. Choice of an organic material is largely influential on various characteristics of organic EL devices, such as efficiency and durability.

Luminescence by organic EL devices is obtained by recombination of charges injected from the respective electrodes in the emitting layer. Therefore, how efficiently the opposite charges (i.e., holes and electrons) are transported to the emitting layer is important in organic EL devices, and the EL devices should have a good charge carrier balance. The probability of recombination of holes and electrons will increase with enhancement of hole injection and enhancement of electron blocking (the ability of stopping electrons injected from the cathode), and high emission efficiency will be obtained by confining the excitons in the emitting layer. The role to be performed by the hole transport material is of significance. Thus, a hole transport material having high hole injection ability, high hole mobility, high electron blocking ability, and high durability to electrons has been sought.

From the viewpoint of device service life, the heat resistance and amorphous properties of materials are also important. Low heat-resistant materials decompose thermally, even in low temperatures, due to the heat generated on driving the device and eventually deteriorate. Materials with low amorphous properties crystallize in a short time in thin film form, thereby deteriorating the device. Hence, materials to be used are required to have high heat resistance and good amorphous properties.

Hole transport materials known for use in organic EL devices include N,N′-diphenyl-N,N′-di(α-naphthyl)benzidine (NPD) and various aromatic amine derivatives (see patent literatures 1 and 2). Although NPD exhibits good hole transporting properties, its glass transition temperature (Tg), which is a measure of heat resistance, is as low as 96° C. so that the device characteristics can reduce in a high temperature atmosphere due to crystallization. Some of the aromatic amine derivatives disclosed in patent literatures 1 and 2 exhibit hole mobility as high as 10⁻³ cm²/Vs or higher but have insufficient electron blocking ability. Organic EL devices using such aromatic amine derivatives allow part of electrons to pass through the emitting layer and, therefore, no improvement on emission efficiency is expected. Accordingly, a material having higher electron blocking ability, higher stability in thin film form, and higher heat resistance has been demanded.

Aromatic tertiary amine compounds represented by the following formulae have been proposed for the improvements on such characteristics as heat resistance, hole injecting properties, hole transporting properties, and electron blocking properties (see patent literatures 3 and 4 below).

While devices using these compounds in the hole injection layer, hole transport layer, or electron blocking layer show improvements on heat resistance and emission efficiency, the effects obtained are still insufficient, and further reduction of driving voltage and higher emission efficiency have been demanded.

In order to improve device characteristics of organic EL devices, an organic EL device having high efficiency based on good carrier balance, a low driving voltage, and a long life could be obtained by combining materials having excellent hole injecting properties, hole transporting properties, electron injecting properties, electron transporting properties, stability in thin film form, and durability.

CITATION LIST Patent Literature

Patent literature 1: JP 3828595

Patent literature 2: JP 3194657

Patent literature 3: JP 4770033

Patent literature 4: WO 2014/060526

SUMMARY OF INVENTION Technical Problem

An object of the invention is to provide, as a material for high-efficient and high-durable organic EL device, an aryldiamine compound having (1) excellent hole transporting properties, (2) stability in thin film form, and (3) high heat resistance.

Another object of the invention is to provide an organic EL device having (1) high emission efficiency and power efficiency, (2) a low driving voltage, and, in particular, (3) a long life by the use of the aryldiamine compound in combination with various materials excellent in hole injecting properties, hole transporting properties, electron injecting properties, electron transporting properties, electron blocking properties, stability in thin film form, and durability in such a manner as to make these materials exhibit their respective characteristics effectively.

Solution to Problem

With the view of accomplishing the above objects, the inventors noted that aryldiamine compounds with a specific structure is excellent in hole injection, hole transport, stability in thin film form, and durability. They have designed and synthesized a variety of aryldiamine compounds and evaluated their characteristics intensively. As a result, they have found an aryldiamine compound having an aryl group at a specific position to be excellent in hole transporting properties and stability in thin film form, and heat resistance.

The inventors have also made various organic EL devices using the aryldiamine compound and evaluated the characteristics of the devices intensively and, as a result, completed the invention.

The invention provides an aryldiamine compound represented by formula (1):

wherein m and n each represent 0 or 1;

Ar¹, Ar², Ar³, and Ar⁴ each represent an aromatic hydrocarbon group or an aromatic heterocyclic group;

when m+n is 0 or 1, and Ar² is an unsubstituted phenyl group, neither Ar³ nor Ar⁴ is an unsubstituted phenyl group; L¹ and L² each represent a single bond, a divalent aromatic hydrocarbon group, or a divalent aromatic heterocyclic group; and

R¹, R², and R³ each represent a hydrogen atom, a deuterium atom, a fluorine atom, a chlorine atom, a cyano group, a nitro group, an alkyl group having 1 to 6 carbon atoms, a cycloalkyl group having 5 to 10 carbon atoms, an alkenyl group having 2 to 6 carbon atoms, an alkoxy group having 1 to 6 carbon atoms, a cycloalkoxy group having 5 to 10 carbon atoms, an aromatic hydrocarbon group, an aromatic heterocyclic group, or an aryloxy group.

Preferred embodiments of the aryldiamine compound of the invention are as follows.

(1) A compound wherein m and n are both zero which is represented by formula (1-1a):

wherein Ar⁵ and Ar⁸ each represent an aromatic hydrocarbon group or an aromatic heterocyclic group;

Ar⁶ and Ar⁷ correspond to Ar² and Ar³ in formula (1), respectively;

when Ar⁶ is an unsubstituted phenyl group, Ar⁷ is not an unsubstituted phenyl group;

R⁴ corresponds to R³ in formula (1);

R⁵⁻⁸ represents multiple groups R⁵, R⁶, R⁷, and R⁸ bonded to the benzene ring at different positions;

R⁹⁻¹² represents multiple groups R⁹, R¹⁰, R¹¹, and R¹² bonded to the benzene ring at different positions; and

R⁵, R⁶, R⁷, R⁸, R⁹, R¹⁰, R¹¹, and R¹² each represent a hydrogen atom, a deuterium atom, a fluorine atom, a chlorine atom, a cyano group, a nitro group, an alkyl group having 1 to 6 carbon atoms, a cycloalkyl group having 5 to 10 carbon atoms, an alkenyl group having 2 to 6 carbon atoms, an alkoxy group having 1 to 6 carbon atoms, a cycloalkoxy group having 5 to 10 carbon atoms, an aromatic hydrocarbon group, an aromatic heterocyclic group, or an aryloxy group.

(2) A compound wherein m and n are both zero which is represented by formula (1-1b):

wherein Ar⁹ and Ar¹⁰ correspond to Ar² and Ar³ in formula (1), respectively;

when Ar⁹ is an unsubstituted phenyl group, Ar¹⁰ is not an unsubstituted phenyl group;

R¹³ corresponds to R³ in formula (1);

R¹⁴⁻¹⁸ represents multiple groups R¹⁴, R¹⁵, R¹⁶, R¹⁷, and R¹⁸ bonded to the benzene ring at different positions;

R¹⁹⁻²² represents multiple groups R¹⁹, R²⁰, R²¹, and R²² bonded to the benzene ring at different positions;

R²³⁻²⁶ represents multiple groups R²³, R²⁴, R²⁵, and R²⁶ bonded to the benzene ring at different positions;

R²⁷⁻³¹ represents multiple groups R²⁷, R²⁸, R²⁹, R³⁰, and R³¹ bonded to the benzene ring at different positions; and

R¹⁴, R¹⁵, R¹⁶, R¹⁷, R¹⁸, R¹⁹, R²⁰, R²¹, R²², R²³, R²⁴, R²⁵, R²⁶, R²⁷, R²⁹, R³⁰, and R³¹ each represent a hydrogen atom, a deuterium atom, a fluorine atom, a chlorine atom, a cyano group, a nitro group, an alkyl group having 1 to 6 carbon atoms, a cycloalkyl group having 5 to 10 carbon atoms, an alkenyl group having 2 to 6 carbon atoms, an alkoxy group having 1 to 6 carbon atoms, a cycloalkoxy group having 5 to 10 carbon atoms, an aromatic hydrocarbon group, an aromatic heterocyclic group, or an aryloxy group.

(3) A compound wherein m=1 and n=0 which is represented by formula (1-2a):

wherein Ar¹ and Ar¹⁴ each represent an aromatic hydrocarbon group or an aromatic heterocyclic group;

Ar¹² and Ar¹³ correspond to Ar² and Ar³ in formula (1), respectively;

when Ar¹² is an unsubstituted phenyl group, Ar¹³ is not an unsubstituted phenyl group;

R³² corresponds to R¹ in formula (1);

R³³ corresponds to R³ in formula (1);

R³⁴⁻³⁷ represents multiple groups R³⁴, R³⁵, R³⁶, and R³⁷ bonded to the benzene ring at different positions;

R³⁸⁻⁴¹ represents multiple groups R³⁸, R³⁹, R⁴⁰, and R⁴¹ bonded to the benzene ring at different positions; and

R³⁴, R³⁵, R³⁶, R³⁷, R³⁸, R³⁹, R⁴⁰, and R⁴¹ each represent a hydrogen atom, a deuterium atom, a fluorine atom, a chlorine atom, a cyano group, a nitro group, an alkyl group having 1 to 6 carbon atoms, a cycloalkyl group having 5 to 10 carbon atoms, an alkenyl group having 2 to 6 carbon atoms, an alkoxy group having 1 to 6 carbon atoms, a cycloalkoxy group having 5 to 10 carbon atoms, an aromatic hydrocarbon group, an aromatic heterocyclic group, or an aryloxy group.

(4) A compound wherein m=1 and n=0 which is represented by formula (1-2b):

wherein Ar¹⁵ and Ar¹⁶ correspond to Ar² and Ar³ in formula (1), respectively;

when Ar¹⁵ is an unsubstituted phenyl group, Ar¹⁶ is not an unsubstituted phenyl group;

R⁴² corresponds to R¹ in formula (1);

R⁴³ corresponds to R³ in formula (1);

R⁴⁴⁻⁴⁸ represents multiple groups R⁴⁴, R⁴⁵, R⁴⁶, R⁴⁷, and R⁴⁸ bonded to the benzene ring at different positions;

R⁴⁹⁻⁵² represents multiple groups R⁴⁹, R⁵⁰, R⁵¹, and R⁵² bonded to the benzene ring at different positions;

R⁵³⁻⁵⁶ represents multiple groups R⁵³, R⁵⁴, R⁵⁵, and R⁵⁶ bonded to the benzene ring at different positions;

R⁵⁷⁻⁶¹ represents multiple groups R⁵⁷, R⁵⁸, R⁵⁹, R⁶⁰, and R⁶¹ bonded to the benzene ring at different positions; and

R⁴⁴, R⁴⁵, R⁴⁶, R⁴⁷, R⁴⁸, R⁴⁹, R⁵⁰, R⁵¹, R⁵², R⁵³, R⁵⁴, R⁵⁵, R⁵⁶, R⁵⁷, R⁵⁸, R⁵⁹, R⁶⁰, and R⁶¹ each represent a hydrogen atom, a deuterium atom, a fluorine atom, a chlorine atom, a cyano group, a nitro group, an alkyl group having 1 to 6 carbon atoms, a cycloalkyl group having 5 to 10 carbon atoms, an alkenyl group having 2 to 6 carbon atoms, an alkoxy group having 1 to 6 carbon atoms, a cycloalkoxy group having 5 to 10 carbon atoms, an aromatic hydrocarbon group, an aromatic heterocyclic group, or an aryloxy group.

(5) A compound wherein m and n are both one which is represented by formula (1-3a):

wherein Ar¹⁷ and Ar²⁰ each represent an aromatic hydrocarbon group or an aromatic heterocyclic group;

Ar¹⁸ and Ar¹⁹ correspond to Ar² and Ar³ in formula (1), respectively;

R⁶² and R⁶³ correspond to R¹ and R² in formula (1), respectively;

R⁶⁴ corresponds to R³ in formula (1);

R⁶⁵⁻⁶⁸ represents multiple groups R⁶⁵, R⁶⁶, R⁶⁷, and R⁶⁸ bonded to the benzene ring at different positions;

R⁶⁹⁻⁷² represent multiple groups R⁶⁹, R⁷⁰, R⁷¹, and R⁷² bonded to the benzene ring at different positions; and

R⁶⁵, R⁶⁶, R⁶⁷, R⁶⁸, R⁶⁹, R⁷⁰, R⁷¹, and R⁷² each represent a hydrogen atom, a deuterium atom, a fluorine atom, a chlorine atom, a cyano group, a nitro group, an alkyl group having 1 to 6 carbon atoms, a cycloalkyl group having 5 to 10 carbon atoms, an alkenyl group having 2 to 6 carbon atoms, an alkoxy group having 1 to 6 carbon atoms, a cycloalkoxy group having 5 to 10 carbon atoms, an aromatic hydrocarbon group, an aromatic heterocyclic group, or an aryloxy group.

(6) A compound wherein m and n are both one which is represented by formula (1-3b):

wherein Ar²¹ and Ar²² correspond to Ar² and Ar³ in formula (1), respectively;

R⁷³ and R⁷⁴ correspond to R¹ and R² in formula (1), respectively;

R⁷⁵ corresponds to R³ in formula (1);

R⁷⁶⁻⁸⁰ represents multiple groups R⁷⁶, R⁷⁷, R⁷⁸, R⁷⁹, and R⁸⁰ bonded to the benzene ring at different positions;

R⁸¹⁻⁸⁴ represents multiple groups R⁸¹, R⁸², R⁸³, and R⁸⁴ bonded to the benzene ring at different positions;

R⁸⁵⁻⁸⁸ represents multiple groups R⁸⁵, R⁸⁶, R⁸⁷, and R⁸⁸ bonded to the benzene ring at different positions;

R⁸⁹⁻⁹³ represents multiple groups R⁸⁹, R⁹⁰, R⁹¹, R⁹², and R⁹³ bonded to the benzene ring at different positions; and

R⁷⁶, R⁷⁷, R⁷⁸, R⁷⁹, R⁸⁰, R⁸¹, R⁸², R⁸³, R⁸⁴, R⁸⁵, R⁸⁶, R⁸⁷, R⁸⁸, R⁸⁹, R⁹⁰, R⁹¹, R⁹², and R⁹³ each represent a hydrogen atom, a deuterium atom, a fluorine atom, a chlorine atom, a cyano group, a nitro group, an alkyl group having 1 to 6 carbon atoms, a cycloalkyl group having 5 to 10 carbon atoms, an alkenyl group having 2 to 6 carbon atoms, an alkoxy group having 1 to 6 carbon atoms, a cycloalkoxy group having 5 to 10 carbon atoms, an aromatic hydrocarbon group, an aromatic heterocyclic group, or an aryloxy group.

In the description of the invention, the aromatic hydrocarbon group, aromatic heterocyclic group, divalent aromatic hydrocarbon group, divalent aromatic heterocyclic group, alkyl group having 1 to 6 carbon atoms, cycloalkyl group having 5 to 10 carbon atoms, alkenyl group having 2 to 6 carbon atoms, alkoxy group having 1 to 6 carbon atoms, cycloalkoxy group having 5 to 10 carbon atoms, and aryloxy group as represented by Ar¹ to Ar²², L¹, L², and R¹ to R⁹³ may be substituted or unsubstituted unless otherwise specified.

Two or more of Ar¹ to Ar²², both of L¹ and L², or two or more of R¹ to R⁹³ which are present in the same molecule, may have the same or different structures.

The aliphatic hydrocarbon groups, such as alkyl, alkenyl, and alkoxy groups, may be either straight or branched unless otherwise noted. The aromatic hydrocarbon group and aromatic heterocyclic group may be monocyclic or polycyclic or may have a fused polycyclic structure unless otherwise defined. Similarly, the divalent aromatic hydrocarbon group or aromatic heterocyclic group may be either monocyclic or polycyclic and may have a fused polycyclic structure unless otherwise specified.

The invention also provides an organic electroluminescent device comprising a pair of electrodes and at least one organic layer disposed between the pair of electrodes, wherein the aryldiamine compound of the invention is used as comprising material of the at least one organic layer.

In preferred embodiments of the organic EL device of the invention, (a) the organic layer is a hole transport layer, (b) the organic layer is an electron blocking layer, (c) the organic layer is a hole injection layer, (d) the organic layer is an emitting layer, and/or (e) the hole transport layer has a dual layer structure composed of a first hole transport layer and a second hole transport layer.

Advantageous Effects of Invention

The aryldiamine compound of the invention is a novel compound and has (1) high hole injecting properties, (2) large hole mobility, (3) excellent electron blocking properties, (4) stability in thin film form, and (5) high heat resistance.

The organic EL device of the invention exhibits (6) high emission efficiency, (7) high power efficiency, (8) low onset voltage, (9) low driving voltage, and (10) long life.

The aryldiamine compound of the invention is suitably used as a material forming a hole transport layer or a hole injection layer of an organic EL device because of its higher hole injecting properties, higher hole mobility, higher electron blocking properties, and higher stability to electrons compared with conventional materials. An organic EL device having a hole transport layer or injection layer formed of the aryldiamine compound of the invention is capable of confining the generated excitons in the emitting layer, thereby providing an increased probability of hole-electron recombination to achieve high emission efficiency, and, at the same time, it drives at a lower voltage and has improved durability.

The aryldiamine compound of the invention is also suited for use as a material forming an electron blocking layer of an organic EL device because of its higher electron blocking ability, higher hole transporting properties, and higher stability in thin film form as compared with conventional materials. An organic EL device having an electron blocking layer formed of the aryldiamine compound of the invention achieves high emission efficiency, a low driving voltage, high current resistance, and a high maximum luminance.

The aryldiamine compound of the invention is also suitable as a material forming an emission layer of an organic EL device. The aryldiamine compound has higher hole transporting properties and a wider band gap than conventional materials. Therefore, the aryldiamine compound can be used as a host material which is doped with a fluorescent or phosphorescent guest material called a dopant to form an emission layer. An organic EL device having such an emission layer drives at a low voltage and achieves improved emission efficiency.

As described, the aryldiamine compound of the invention is useful as a material forming the hole injection layer, hole transport layer, electron blocking layer, or emission layer of an organic EL device, exhibiting large hole mobility, excellent electron blocking ability, stability in thin film form, and high heat resistance. The organic EL device of the invention has high emission efficiency and high power efficiency and, therefore, realizes reductions in driving voltage and onset voltage. It also enjoys high durability and long service life.

BRIEF DESCRIPTION OF DRAWINGS

FIG. 1 is a ¹H-NMR spectrum of Compound 1-2 of Example 1.

FIG. 2 is a ¹H-NMR spectrum of Compound 2-1 of Example 2.

FIG. 3 is a ¹H-NMR spectrum of Compound 2-4 of Example 3.

FIG. 4 illustrates the structure of the organic EL devices of Device Examples 1 to 3 and Comparative Device Examples 1 to 4.

FIG. 5 illustrates structural formulae of Compounds 1-1 through 1-8 which are the aryldiamine compounds.

FIG. 6 illustrates structural formulae of Compounds 1-9 through 1-14 which are the aryldiamine compounds.

FIG. 7 illustrates structural formulae of Compounds 1-15 through 1-22 which are the aryldiamine compounds.

FIG. 8 illustrates structural formulae of Compounds 1-23 through 1-30 which are the aryldiamine compounds.

FIG. 9 illustrates structural formulae of Compounds 1-31 and 1-32 which are the aryldiamine compounds.

FIG. 10 illustrates structural formulae of Compounds 2-1 through 2-8 which are the aryldiamine compounds.

FIG. 11 illustrates structural formulae of Compounds 2-9 through 2-16 which are the aryldiamine compounds.

FIG. 12 illustrates structural formulae of Compounds 2-17 through 2-22 which are the aryldiamine compounds.

FIG. 13 illustrates structural formulae of Compounds 2-23 through 2-30 which are the aryldiamine compounds.

FIG. 14 illustrates structural formulae of Compounds 2-31 through 2-36 which are the aryldiamine compounds.

FIG. 15 illustrates structural formulae of Compounds 3-1 to 3-10 which are the aryldiamine compounds.

FIG. 16 illustrates structural formulae of Compounds 3-11 through 3-14 which are the aryldiamine compounds.

DESCRIPTION OF EMBODIMENTS [I] Aryldiamine Compounds

The invention provides a novel aryldiamine compound which has two amino groups linked via a specific phenylene, biphenylene, or triphenylene group and which is represented by formula (1):

The aryldiamine compound of formula (1) include three embodiments: a compound represented by formula (1-1a) below, a compound represented by formula (1-2a) below, and a compound represented by formula (1-3a) below. Each embodiment is specified by the m and n values and L¹, L², Ar¹, and Ar⁴ definitions in formula (1).

The compound represented by formula (1-1a) is an embodiment of formula (1), in which m is 0, n is 0, L¹ is a single bond, L² is a single bond, Ar¹ is a phenyl group substituted by Ar⁵ and R⁵⁻⁸, and Ar⁴ is a phenyl group substituted by Ar⁸ and R⁹⁻¹².

The compound represented by formula (1-2a) is an embodiment of formula (1), in which m is 1, n is 0, L¹ is a single bond, L² is a single bond, Ar¹ is a phenyl group substituted by Ar¹¹ and R³⁴⁻³⁷, and Ar⁴ is a phenyl group substituted by Ar¹⁴ and R³⁸⁻⁴¹.

The compound represented by formula (1-3a) is an embodiment of formula (1), in which m is 1, n is 1, L¹ is a single bond, L² is a single bond, Ar¹ is a phenyl group substituted by Ar¹⁷ and R⁶⁵⁻⁶⁸, and Ar⁴ is a phenyl group substituted by Ar²⁰ and R⁶⁹⁻⁷².

Ar⁶ and Ar⁷ in formula (1-1a) correspond to Ar² and Ar³ in formula (1), respectively.

Ar¹² and Ar¹³ in formula (1-2a) correspond to Ar² and Ar³ in formula (1), respectively.

Ar¹⁸ and Ar¹⁹ in formula (1-3a) correspond to Ar² and Ar³ in formula (1), respectively.

R⁴ in formula (1-1a) corresponds to R³ in formula (1).

R³² in formula (1-2a) corresponds to R¹ in formula (1).

R³³ in formula (1-2a) corresponds to R³ in formula (1).

R⁶² and R⁶³ in formula (1-3a) correspond to R¹ and R² in formula (1), respectively.

R⁶⁴ in formula (1-3a) corresponds to R³ in formula (1).

In formula (1-1a), R⁵⁻⁸ represents multiple groups R⁵, R⁶, R⁷, and R⁸ bonded to the benzene ring at different positions, and R⁹⁻¹² represents multiple groups R⁹, R¹⁰, R¹¹, and R¹² bonded to the benzene ring at different positions.

In formula (1-2a), R³⁴⁻³⁷ represents multiple groups R³⁴, R³⁵, R³⁶, and R³⁷ bonded to the benzene ring at different positions, and R³⁸⁻⁴¹ represents multiple groups R³⁸, R³⁹, R⁴⁰, and R⁴¹ bonded to the benzene ring at different positions.

In formula (1-3a), R⁶⁵⁻⁶⁸ represents multiple groups R⁶⁵, R⁶⁶, R⁶⁷, and R⁶⁸ bonded to the benzene ring at different positions, and R⁶⁹⁻⁷² represents multiple groups R⁶⁹, R⁷⁰, R⁷¹, and R⁷² bonded to the benzene ring at different positions.

The aryldiamine compounds of formulae (1-1a), (1-2a), and (1-3a) include three embodiments: a compound represented by formula (1-1b) below, a compound represented by formula (1-2b) below, and a compound represented by formula (1-3b) below, respectively. Each embodiment is specified by the structures of Ar¹ and Ar⁴ in formula (1).

The compound represented by formula (1-1b) is an embodiment of formula (1), in which Ar¹ is a biphenylyl group substituted by R¹⁴⁻¹⁸ and R¹⁹⁻²², and Ar⁴ is a biphenylyl group substituted by R²³⁻²⁶ and R²⁷⁻³¹.

The compound represented by formula (1-2b) is an embodiment of formula (1), in which Ar¹ is a biphenylyl group substituted by R⁴⁴⁻⁴⁸ and R⁴⁹⁻⁵², and Ar⁴ is a biphenylyl group substituted by R⁵³⁻⁵⁶ and R⁵⁷⁻⁶¹.

The compound represented by formula (1-3b) is an embodiment of formula (1), in which Ar¹ is a biphenylyl group substituted by R⁷⁶⁻⁸⁰ and R⁸¹⁻⁸⁴, and Ar⁴ is a biphenylyl group substituted by R⁸⁵⁻⁸⁸ and R⁸⁹⁻⁹³.

Ar⁹ and Ar¹⁰ in formula (1-1b) correspond to Ar² and Ar³ in formula (1), respectively, and to Ar⁶ and Ar⁷ in formula (1-1a), respectively.

Ar¹⁵ and Ar¹⁶ in formula (1-2b) correspond to Ar² and Ar³ in formula (1), respectively, and to Ar¹² and Ar¹³ in formula (1-2a), respectively.

Ar²¹ and Ar²² in formula (1-3b) correspond to Ar² and Ar³ in formula (1), respectively, and to Ar¹⁸ and Ar¹⁹ in formula (1-3a), respectively.

R¹³ in formula (1-1b) corresponds to R³ in formula (1) and R⁴ in formula (1-1a).

R⁴² in formula (1-2b) corresponds to R¹ in formula (1) and R³² in formula (1-2a).

R⁴³ in formula (1-2b) corresponds to R³ in formula (1) and R³³ in formula (1-2a).

R⁷³ and R⁷⁴ in formula (1-3b) correspond to R¹ and R² in formula (1), respectively, and to R⁶² and R⁶³ in formula (1-3a), respectively.

R⁷⁵ in formula (1-3b) corresponds to R³ in formula (1) and R⁶⁴ in formula (1-3a).

In formula (1-1b), R¹⁴⁻¹⁸ represents multiple groups R¹⁴, R¹⁵, R¹⁶, R¹⁷, and R¹⁸ bonded to the benzene ring at different positions; R¹⁹⁻²² represents multiple groups R¹⁹, R²⁰, R²¹, and R²² bonded to the benzene ring at different positions; R²³⁻²⁶ represents multiple groups R²³, R²⁴, R²⁵, and R²⁶ bonded to the benzene ring at different positions; and R²⁷⁻³¹ represents multiple groups R²⁷, R²⁸, R²⁹, R³⁰, and R³¹ bonded to the benzene ring at different positions.

In formula (1-2b), R⁴⁴⁻⁴⁸ represents multiple groups R⁴⁴, R⁴⁵, R⁴⁶, R⁴⁷, and R⁴⁸ bonded to the benzene ring at different positions; R⁴⁹⁻⁵² represents multiple groups R⁴⁹, R⁵⁰, R⁵¹, and R⁵² bonded to the benzene ring at different positions; R⁵³⁻⁵⁶ represents multiple groups R⁵³, R⁵⁴, R⁵⁵, and R⁵⁶ bonded to the benzene ring at different positions; and R⁵⁷⁻⁶¹ represents multiple groups R⁵⁷, R⁵⁸, R⁵⁹, R⁶⁰, and R⁶¹ bonded to the benzene ring at different positions.

In formula (1-3b), R⁷⁶⁻⁸⁰ represents multiple groups R⁷⁶, R⁷⁷, R⁷⁸, R⁷⁹, and R⁸⁰ bonded to the benzene ring at different positions; R⁸¹⁻⁸⁴ represents multiple groups R⁸¹, R⁸², R⁸³, and R⁸⁴, R⁸⁵⁻⁸⁸ represents multiple groups R⁸⁵, R⁸⁶, R⁸⁷, and R⁸⁸ bonded to the benzene ring at different positions; and R⁸⁹⁻⁹³ represents multiple groups R⁸⁹, R⁹⁰, R⁹¹, R⁹², and R⁹³ bonded to the benzene ring at different positions.

(m, n)

m and n each represent an integer 0 or 1.

(Ar¹ to Ar²²)

A¹ through Ar²² each represent an aromatic hydrocarbon group or an aromatic heterocyclic group.

Note that, when in formula (1) Ar² is an unsubstituted phenyl group, and m+n=0 or 1, neither Ar³ nor Ar⁴ is an unsubstituted phenyl group.

Accordingly, in formula (1-1a), when Ar⁶ is an unsubstituted phenyl group, Ar⁷ is not an unsubstituted phenyl group. In formula (1-1b), when Ar⁹ is an unsubstituted phenyl group, Ar¹⁰ is not an unsubstituted phenyl group.

Similarly, in formula (1-2a), when Ar¹² is an unsubstituted phenyl group, Ar¹³ is not an unsubstituted phenyl group. In formula (1-2b), when Ar¹⁵ is an unsubstituted phenyl group, Ar¹⁶ is not an unsubstituted phenyl group.

Examples of the aromatic hydrocarbon group or aromatic heterocyclic group as represented by Ar¹ through Ar²² include aryl groups having 6 to 30 carbon atoms and heteroaryl groups having 2 to 20 carbon atoms, such as phenyl, biphenylyl, terphenylyl, naphthyl, anthracenyl, phenanthrenyl, fluorenyl, spirobifluorenyl, indenyl, pyrenyl, perylenyl, fluoranthenyl, triphenylenyl, pyridyl, pyrimidinyl, triazinyl, furyl, pyrrolyl, thienyl, quinolyl, isoquinolyl, benzofuranyl, benzothienyl, indolyl, carbazolyl, benzoxazolyl, benzothiazolyl, quinoxalinyl, benzimidazolyl, pyrazolyl, dibenzofuranyl, dibenzothienyl, naphthylidinyl, acridinyl, and carbolinyl.

The aromatic hydrocarbon group or aromatic heterocyclic group represented by Ar¹ to Ar²² may optionally be substituted. Examples of substituents include a deuterium atom, a cyano group, a nitro group, and, in addition, the following atoms and groups:

Halogen atoms, such as fluorine, chlorine, bromine, and iodine; alkyl groups having 1 to 6 carbon atoms, such as methyl, ethyl, n-propyl, isopropyl, n-butyl, isobutyl, tert-butyl, n-pentyl, isopentyl, neopentyl, and n-hexyl; alkoxy groups having 1 to 6 carbon atoms, such as methoxy, ethoxy, and propoxy; alkenyl groups, such as vinyl and allyl; aryloxy groups, such as phenoxy and tolyloxy; arylalkoxy groups, such as benzoyloxy and phenethyloxy; aromatic hydrocarbon groups, such as phenyl, biphenylyl, terphenylyl, naphthyl, anthracenyl, phenanthrenyl, fluorenyl, indenyl, pyrenyl, perylenyl, fluoranthenyl, and triphenylenyl; aromatic heterocyclic groups, such as pyridyl, pyrimidinyl, triazinyl, thienyl, furyl, pyrrolyl, quinolyl, isoquinolyl, benzofuranyl, benzothienyl, indolyl, carbazolyl, benzoxazolyl, benzothiazolyl, quinoxalinyl, benzimidazolyl, pyrazolyl, dibenzofuranyl, dibenzothienyl, and carbolinyl; arylvinyl groups, such as styryl and naphthylvinyl; and acyl groups, such as acetyl and benzoyl.

These substituents may be independent of one another or may be connected via a single bond, a substituted or unsubstituted methylene group, an oxygen atom, or a sulfur atom to form a ring.

L¹ and L² each represent a single bond, a divalent aromatic hydrocarbon group, or a divalent aromatic heterocyclic group.

The divalent aromatic hydrocarbon group or divalent aromatic heterocyclic group as represented by L¹ and L² is a divalent group derived by removing two hydrogen atoms from an aromatic hydrocarbon or an aromatic heterocyclic ring, respectively.

Examples of the aromatic hydrocarbons and aromatic heterocyclic rings from which L¹ and L² are derived include benzene, biphenyl, terphenyl, naphthalene, anthracene, phenanthrene, fluorene, spirobifluorene, indane, pyrene, perylene, fluoranthene, triphenylene, pyridine, pyrimidine, triazine, furan, pyrrole, thiophene, quinoline, isoquinoline, benzofuran, benzothiophene, indoline, carbazole, benzoxazole, benzothiazole, quinoxaline, benzimidazole, pyrazole, dibenzofuran, dibenzothiophene, naphthyridine, and acridine.

The divalent aromatic hydrocarbon group or divalent aromatic heterocyclic group as represented by L¹ and L² may optionally be substituted. Examples of substituents include those recited above as substituents on the aromatic hydrocarbon group or aromatic heterocyclic group represented by Ar¹ to Ar²². Embodiments that the substituents on L¹ and L² may have are the same as the embodiments the substituents on Ar¹ to Ar²² may have.

(R¹ through R⁹³)

R¹ through R⁹³ each represent a hydrogen atom, a deuterium atom, a fluorine atom, a chlorine atom, a cyano group, a nitro group, an alkyl group having 1 to 6 carbon atoms, a cycloalkyl group having 5 to 10 carbon atoms, an alkenyl group having 2 to 6 carbon atoms, an alkoxy group having 1 to 6 carbon atoms, a cycloalkoxy group having 5 to 10 carbon atoms, an aromatic hydrocarbon group, an aromatic heterocyclic group, or an aryloxy group.

Examples of the alkyl groups having 1 to 6 carbon atoms, cycloalkyl groups having 5 to 10 carbon atoms, and alkenyl groups having 2 to 6 carbon atoms as R¹ to R⁹³ include methyl, ethyl, n-propyl, isopropyl, n-butyl, isobutyl, tert-butyl, n-pentyl, isopentyl, neopentyl, n-hexyl, cyclopentyl, cyclohexyl, 1-adamantyl, 2-adamantyl, vinyl, allyl, isopropenyl, and 2-butenyl.

Examples of the alkoxy groups having 1 to 6 carbon atoms and cycloalkoxy groups having 5 to 10 carbon atoms as R¹ to R⁹³ include methoxy, ethoxy, n-propoxy, isopropoxy, n-butoxy, tert-butoxy, n-pentyloxy, n-hexyloxy, cyclopentyloxy, cyclohexyloxy, cycloheptyloxy, cyclooctyloxy, 1-adamantyloxy, and 2-adamantyloxy.

Examples of the aromatic hydrocarbon group or aromatic heterocyclic group as R¹ to R⁹³ include those enumerated above as examples of Ar¹ to Ar²².

Examples of the aryloxy group as R¹ to R⁹³ include phenoxy, biphenylyloxy, terphenylyloxy, naphthyloxy, anthracenyloxy, phenanthrenyloxy, fluorenyloxy, indenyloxy, pyrenyloxy, and perylenyloxy.

The alkyl groups having 1 to 6 carbon atoms, cycloalkyl groups having 5 to 10 carbon atoms, alkenyl groups having 2 to 6 carbon atoms, alkoxy groups having 1 to 6 carbon atoms, cycloalkoxy groups having 5 to 10 carbon atoms, aromatic hydrocarbon group, aromatic heterocyclic group, and aryloxy group as represented by R¹ to R⁹³ may be optionally substituted. Examples of substituents include those recited above as substituents on the aromatic hydrocarbon groups or aromatic heterocyclic groups represented by Ar¹ to Ar²². Embodiments that the substituents on R¹ to R⁹³ may have are the same as the embodiments that the substituents on A¹ to Ar²² may have.

PREFERRED EMBODIMENTS

Preferred embodiments of the aryldiamine compounds will then be described.

Preferred of the aryldiamine compounds of the invention are those of formulae (1-1a), (1-2a), and (1-3a), and more preferred are those of formulae (1-1b), (1-2b), and (1-3b).

The aryldiamine compounds are preferably symmetric. As used herein, the term “symmetric” means having the following structures.

In the case of the compounds of formula (1-1a), Ar⁶ and Ar⁷ have the same structure inclusive of the kind and position of their substituents, and the combination of Ar⁵ and the phenyl group substituted by R⁵⁻⁸ and the combination of Ar⁸ and the phenyl group substituted by R⁹⁻¹² also have the same structure inclusive of the kind and position of their substituents. The same applies to the formula (1-1b).

In the case of the compounds of formula (1-2a), Ar¹² and Ar¹³ have the same structure inclusive of the kind and position of their substituents; the combination of Ar¹¹ and the phenyl group substituted by R³⁴⁻³⁷ and the combination of Ar¹⁴ and the phenyl group substituted by R³⁸⁻⁴¹ have the same structure inclusive of the kind and position of their substituents; and R³² and R³³ are the same in both kind and position with respect to the amino group on the respective benzene rings to which they are bonded. The same applies to the formula (1-2b).

In the case of the compounds of formula (1-3a), Ar¹⁸ and Ar¹⁹ have the same structure inclusive of the kind and position of their substituent; the combination of Ar¹⁷ and the phenyl group substituted by R⁶⁵⁻⁶⁸ and the combination of Ar²⁰ and the phenyl group substituted by R⁶⁹⁻⁷² have the same structure inclusive of the kind and position of their substituents; and R⁶² and R⁶⁴ are the same in both kind and position with respect to the amino group on the respective benzene rings to which they are bonded. The same applies to the formula (1-3b).

Ar² and Ar³ are each preferably an aromatic hydrocarbon group, more preferably the one having two or more aromatic rings, such as biphenylyl, terphenylyl, naphthyl, triphenylenyl, spirobifluorenyl, or fluorenyl. The biphenylyl, terphenylyl, triphenylenyl, and spirobifluorenyl groups are preferably unsubstituted. The naphthyl group is preferably unsubstituted or substituted by an aromatic hydrocarbon group, more preferably unsubstituted. The aromatic hydrocarbon group as a substituent on the naphthyl group is preferably selected from phenyl, biphenylyl, and terphenylyl. The fluorenyl group preferably has a substituent. The substituent on the fluorenyl group is preferably methyl or phenyl, more preferably methyl.

Ar⁶, Ar⁷, Ar⁹, and Ar¹⁰ are each preferably an aromatic hydrocarbon group, more preferably the one having two or more aromatic rings, such as biphenylyl, terphenylyl, naphthyl, triphenylenyl, spirobifluorenyl, or fluorenyl. The biphenylyl, terphenylyl, triphenylenyl, and spirobifluorenyl groups are preferably unsubstituted. The naphthyl group may be substituted. The substituent on the naphthyl group is preferably an aromatic hydrocarbon group, more preferably phenyl, biphenylyl, or terphenylyl. The fluorenyl group preferably has a substituent. The substituent on the fluorenyl group is preferably methyl or phenyl, more preferably methyl.

Ar¹², Ar¹³, Ar¹⁵, and Ar¹⁶ are each preferably an aromatic hydrocarbon group, more preferably the one having two or more aromatic rings, such as biphenylyl, terphenylyl, naphthyl, triphenylenyl, spirobifluorenyl, or fluorenyl. From the viewpoint of heat resistance, in particular, the one having two or more aromatic rings and a fused polycyclic structure, such as triphenylenyl, spirobifluorenyl, or fluorenyl, is preferred. From the viewpoint of emission efficiency and long life, the one having two or more aromatic rings and no fused polycyclic structure, such as biphenylyl or terphenylyl, is preferred. The biphenylyl, terphenylyl, naphthyl, triphenylenyl, and spirobifluorenyl groups are preferably unsubstituted. The fluorenyl group preferably has a substituent. The substituent on the fluorenyl group is preferably methyl or phenyl, more preferably methyl.

Ar¹⁸, Ar⁹, Ar²¹, and Ar²² are each preferably an aromatic hydrocarbon group, more preferably the one having two or more aromatic rings, such as biphenylyl, terphenylyl, naphthyl, triphenylenyl, spirobifluorenyl, or fluorenyl. The biphenylyl, terphenylyl, naphthyl, triphenylenyl, and spirobifluorenyl groups are preferably unsubstituted. The fluorenyl group preferably has a substituent. The substituent on the fluorenyl group is preferably methyl or phenyl, more preferably methyl.

Ar¹ and Ar⁴ are each preferably an aromatic hydrocarbon group, more preferably the one having no fused polycyclic structure. Specifically, Ar¹ and Ar⁴ are each preferably phenyl, biphenylyl, terphenylyl, triphenylenyl, or fluorenyl, more preferably phenyl, biphenylyl, or terphenylyl, even more preferably biphenylyl. The groups as Ar¹ and Ar⁴ are preferably unsubstituted or substituted by a substituent other than an aromatic heterocyclic group, more preferably unsubstituted. The substituent other than an aromatic heterocyclic group is preferably phenyl, naphthyl, or methyl.

Ar⁵ and Ar⁸ are each preferably an aromatic hydrocarbon group, more preferably the one having no fused polycyclic structure, such as phenyl or naphthyl, even more preferably phenyl. The groups as Ar⁵ and Ar⁸ are preferably unsubstituted.

Ar¹¹ and Ar¹⁴ are each preferably an aromatic hydrocarbon group, more preferably the one having no fused polycyclic structure. Specifically, Ar¹¹ and Ar¹⁴ are each preferably phenyl, biphenylyl, or naphthyl, more preferably phenyl or biphenylyl, even more preferably phenyl. The groups as Ar¹¹ and Ar¹⁴ are preferably unsubstituted.

Ar¹⁷ and Ar²⁰ are each preferably an aromatic hydrocarbon group, more preferably the one having no fused polycyclic structure, such as phenyl or biphenylyl. The groups as Ar¹⁷ and Ar²⁰ are preferably unsubstituted or substituted by a substituent other than an aromatic heterocyclic group, more preferably unsubstituted.

L¹ and L² are each preferably a single bond.

R¹ through R⁴, R¹³, R³², R³³, R⁴², R⁴³, R⁶² through R⁶⁴, and R⁷³ through R⁷⁵ are each preferably hydrogen, deuterium, or an aromatic hydrocarbon group, more preferably hydrogen, deuterium, or phenyl, even more preferably hydrogen or deuterium.

R⁵ through R¹², R¹⁴ through R³¹, R³⁴ through R⁴¹, R⁴⁴ through R⁶¹, R⁶⁵ through R⁷², and R⁷⁶ through R⁹³ are each preferably hydrogen, deuterium, or an aromatic hydrocarbon group, more preferably hydrogen, deuterium, or phenyl, even more preferably hydrogen or deuterium.

Specific, but non-limiting, examples of preferred aryldiamine compounds of the invention are shown in FIGS. 5 through 16.

In Compounds 1-1 to 1-32 that are composed of two amino groups linked via a phenylene group, the two substituents each drawn above each one of the nitrogen atoms on the plane of the paper corresponds to -L¹-Ar¹ and -L²-Ar⁴ in formula (1), and the two substituents each drawn below each one of the nitrogen atoms correspond to Ar² and Ar³ in formula (1).

In Compounds 2-1 to 2-36 that are composed of two amino groups linked via a biphenylene group, the substituent below the left (on the paper) nitrogen atom and the substituent above the right nitrogen atom correspond to -L¹-Ar¹ and -L²-Ar⁴ in formula (1), and the substituent above the left nitrogen atom and the substituent below the right nitrogen atom correspond to Ar² and Ar³ in formula (1).

In Compounds 3-1 through 3-14 that are composed of two amino groups linked via a triphenylene group, the two substituents below (on the paper) the nitrogen atoms correspond to -L¹-Ar¹ and -L²-Ar⁴ in formula (1), and the two substituents above the nitrogen atoms correspond to Ar² and Ar³ in formula (1).

Compounds 1-1 to 1-19, 1-21, 1-22, 1-27, and 1-32 belong to formulae (1-1a) and (1-1b), and Compounds 1-25 and 1-26 belong to formula (1-1a).

Compounds 2-1 to 2-5, 2-9 to 2-12, 2-15 to 2-21, 2-23 to 2-26, and 2-28 to 2-31 belong to formulae (1-2a) and (1-2b), and Compounds 2-7, 2-8, and 2-27 belong to formula (1-2a).

Compounds 3-1 and 3-3 to 3-8 belong to formulae (1-3a) and (1-3b), and Compound 3-12 belong to formula (1-3a).

[II] Method of Preparation

The aryldiamine compounds of the invention can be prepared through known processes. For example, the aryldiamine compound may be obtained by cross coupling reaction in the presence of a copper catalyst between a dihalide of a compound having a phenylene, biphenylene or terphenylene structure that is to link the two amino groups of a desired aryldiamine compound and a secondary amine having an aromatic hydrocarbon group or aromatic heterocyclic group bonded to its nitrogen atom.

The crude aryldiamine compound thus prepared can be purified by, for example, column chromatography, adsorption using silica gel, activated carbon, or activated clay, or recrystallization or crystallization from solvents. Purification may also be carried out by sublimation. Identification of the product may be confirmed by NMR analysis. Physical characterization of the aryldiamine compound can be performed by the measurement of melting temperature, glass transition temperature (Tg), work function, and the like.

Melting temperature is a measure of ease of evaporation. The melting point can be measured on a powder sample using a high-sensitivity differential scanning calorimeter (DSC 3100SA, from Bruker AXS).

Glass transition temperature (Tg) is a measure of stability in thin film form. The Tg can be measured in the same manner as for melting temperature.

Work function is a measure of hole transporting or blocking properties. The work function can be measured on a 100 nm-thick film formed on an ITO substrate using an ionization potential measuring device (PYS-202, available from Sumitomo Heavy Industries, Ltd.).

[III] Organic EL Device

The organic EL device basically comprises a spaced pair of electrodes and at least one organic layer disposed therebetween.

The organic EL device of the invention may take various configurations as long as it has the above described basic structure. For example, it may be a layer structure which has a substrate, an anode, a hole injection layer, a hole transport layer, an emitting layer, an electron transport layer, and a cathode stacked in that order. It may additionally have an electron blocking layer between the hole transport layer and the emitting layer, a hole blocking layer between the emitting layer and the electron transport layer, or an electron injection layer between the electron transport layer and the cathode. Furthermore, some organic layers may be omitted, or some functions may be performed by a single organic layer. For example, an organic layer may combine features of the hole injection layer and hole transport layer or may combine features of the electron injection layer and electron transport layer. It is also possible that two or more organic layers having the same function may be stacked one on another. For example, the organic EL device may have a duel hole transport layer, a dual emitting layer, a dual electron transport layer, and the like. The organic EL device of the invention preferably has a dual hole transport layer composed of a first hole transport layer and a second hole transport layer. FIG. 4 illustrates the stacked layer structure adopted in Examples described layer, which is composed of a glass substrate 1, a transparent anode 2, a hole injection layer 3, a first hole transport layer 4, a second hole transport layer 5, an emitting layer 6, an electron transport layer 7, an electron injection layer 8, and a cathode 9 in the order described.

While the individual layers will be described layer in detail, note that the organic EL device of the invention is characterized by containing the aryldiamine compound in at least one organic layer.

Anode:

The anode 2 may be formed of any electrode materials known per se. For example, electrode materials with large work functions, such as ITO and gold, are used.

Hole Injection Layer:

The hole injection layer 3 may preferably contain the aryldiamine compound of the invention. Other known materials may be used in place of, or in admixture or combination with, the aryldiamine compound.

Examples of useful known materials include star-burst triphenylamine derivatives and various triphenylamine tetramers; porphyrin compounds typified by copper phthalocyanine; acceptor type heterocyclic compounds, such as hexacyanoazatriphenylene; and solution-processed polymeric materials.

A material commonly used to form the hole injection layer and having been p-doped with trisbromophenylamine hexachloroantimony; a radialene derivative (see WO 2014/009310), or the like; or a polymer having the structure of a benzidine derivative, such as TPD, as a partial structure thereof may also be used.

The hole injection layer 3 can be formed by thin film formation processes, such as evaporation deposition, spin coating, and ink-jet printing, using the material described above. Similarly, other layers described below can each be formed by known thin film formation processes, such as evaporation deposition, spin coating, and ink-jet printing.

Hole Transport Layer:

A hole transport layer is provided on the hole injection layer 3. The hole transport layer may be a single layer but is preferably a stacked dual layer composed of a first hole transport layer 4 on the side of the hole injection layer and a second hole transport layer 5 on the side of the emitting layer.

The hole transport layer preferably contains the aryldiamine compound of the invention. Where the hole transport layer has a dual layer structure, the aryldiamine compound of the invention may be used in either one or both of the two layers under the condition that the two layers are different in composition.

The aryldiamine compound of the invention may be replaced with, or used in admixture or combination with, known materials, such as benzidine derivatives, e.g., N,N′-diphenyl-N,N′-di(m-tolyl)benzidine(TPD), N,N-diphenyl-N,N′-di(t-naphthyl)benzidine (NPD), N,N,N′,N′-tetrabiphenylylbenzidine, and 1,1-bis[4-(di-4-tolylamino)phenyl]cyclohexane (TAPC); and trimers and tetramers of various triphenylamine compounds.

The hole transport layer may be formed of a single material or a mixture of materials including the single material. The hole transport layer may have a multi-layer structure composed of (a) layers each formed of a single material, (b) layers each formed of a mixture of materials, or (c) a layer formed of a single material and a layer formed of a mixture of materials. The same structure is applicable to organic layers other than the hole transport layer.

A hole injection/transport layer may be formed using a solution-processed polymer, such as poly(3,4-ethylenedioxythiophene)/poly(styrene sulfonate) (PEDOT/PSS).

A material commonly used to make the hole transport layer and having been p-doped with trisbromophenylamine hexachloroantimony, a radialene derivative (see WO 2014/009310), or the like, or a polymer having the structure of a benzidine derivative, such as TPD, as a partial structure thereof may also be used.

Electron Blocking Layer:

The aryldiamine compound of the invention is also suited to form an electron blocking layer (not shown). Other known electron blocking materials are also useful, including carbazole derivatives, such as 4,4′,4″-tri(N-carbazolyl)triphenylamine (TCTA), 9,9-bis[4-(carbazol-9-yl)phenyl]fluorene, 1,3-bis(carbazol-9-yl)benzene (mCP), and 2,2-bis(4-carbazol-9-ylphenyl)adamantane (Ad-Cz); and triarylamines compounds having a triphenylsilyl group, such as 9-[4-(carbazol-9-yl)phenyl]-9-[4-(tolyphenylsilyl)phenyl]-9H-fluorene.

Emitting Layer:

The aryldiamine compound is also suitable to make the emitting layer 6. Other known light-emitting materials are also useful. Examples of the known materials include quinolinol derivative metal complexes, such as Alq₃, other various metal complexes, anthracene derivatives, bisstyrylbenzene derivatives, pyrene derivatives, oxazole derivatives, and poly(p-phenylenevinylene) derivatives.

The emitting layer 6 may be formed of a host material and a dopant material. Examples of the host material include: the aryldiamine compound of the invention, the above described light-emitting materials; heterocyclic compounds having an indole ring as a part of their fused ring system; heterocyclic compounds having a carbazole ring as a part of their fused ring system; carbazole derivatives; thiazole derivatives; benzimidazole derivatives; polydialkylfuorene derivatives; and anthracene derivatives. Examples of the dopant material include amine derivatives having a fluorene ring as a part of their fused ring system; quinacridone, coumarin, rubrene, perylene, pyrene, and their derivatives; benzopyran derivatives; indenophenanthrene derivatives; rhodamine derivatives; and aminostyryl derivatives.

Phosphorescent materials are also useful as a light-emitting material. The phosphorescent materials include iridium complexes and platinum complexes. Examples of the phosphorescent materials include green phosphorescent materials, such as Ir(ppy)₃, blue phosphorescent materials, such as FIrpic and FIr6, and red phosphorescent materials, such as Btp₂Ir(acac).

The host material to be doped by the phosphorescent material include carbazole derivatives, such as 4,4′-di(N-carbazolyl)biphenyl (CBP), TCTA, and mCP, as hole injecting/transporting host materials; and p-bis(triphenylsilyl)benzene (UGH2) and 2,2′,2″-(1,3,5-phenylene)-tris(1-phenyl-1H-benzimidazole) (TPBI) as electron transporting host materials. Use of such hot materials provides high-performance organic EL derives.

Doping of the host material with the phosphorescent material is preferably carried out by co-depositing the phosphorescent material in an amount ranging from 1 to 30 wt % relative to the whole emitting layer so as to avoid concentration quenching.

A delayed fluorescence emitter, including CDCB derivatives, such as PIC-TRZ, CC2TA, PXZ-TRZ, and 4CzIPN, may also be used as a light-emitting material.

Hole Blocking Layer:

A hole blocking layer (not shown) may be provided on the emitting layer 5. The hole blocking layer may be formed of a known compound having a hole blocking effect. Examples of such a known compound include phenanthroline derivatives, such as bathocuproine (BCP); quinolinol derivative metal complexes, such as aluminum (III) 4-biphenylolate 2-methyl-8-quinolinolate (BAlq); various rare earth complexes; triazole derivatives; triazine derivatives; and oxadiazole derivatives. These materials may also serve as a material of the electron transport layer.

Electron Transport Layer:

The electron transport layer 7 may be formed of a known electron transporting material. Examples of useful known electron transporting materials include quinolinol derivative metal complexes, such as Alq₃ and BAlq; other various metal complexes; triazole derivatives; triazine derivatives; oxadiazole derivatives; pyridine derivatives; pyrimidine derivatives; benzimidazole derivatives; thiadiazole derivatives; anthracene derivatives; carbodiimide derivatives; quinoxaline derivatives; pyridoindole derivatives; phenanthroline derivatives; and silole derivatives.

Electron Injection Layer:

The electron injection layer 8 may be formed of, for example, an alkali metal salt, such as lithium fluoride or cesium fluoride; an alkaline earth metal salt, such as magnesium fluoride; or a metal oxide, such as aluminum oxide. As long as the materials of the electron transport layer and the cathode are suitably chosen, the electron injection layer may be omitted.

Cathode:

The cathode 9 may be formed of an electrode material with a low work function, such as aluminum, or an alloy with a still lower work function, such as magnesium-silver alloy, magnesium-indium alloy, or aluminum-magnesium alloy.

EXAMPLES

The invention will now be illustrated in greater detail with reference to Examples, but it should be understood that the invention is not construed as being limited thereto.

Example 1—Compound 1-2 Synthesis of 1,2-bis[biphenyl-4-yl(9,9-dimethyl-9H-fluoren-2-yl)amino]benzene

In a reaction vessel purged with nitrogen were put 24.1 g of biphenyl-4-yl(9,9-dimethyl-9H-fluoren-2-yl)amine, 10.0 g of 1,2-diiodobenzene, 0.2 g of copper powder, 10.5 g of potassium carbonate, and 10 ml of dodecylbenzene. The mixture was stirred under reflux for 72 hours. The resulting reaction mixture was cooled, toluene added thereto to conduct extraction, and the extract filtered to remove insoluble solid, followed by concentration. The concentrate was purified by column chromatography using silica gel as stationary phase and toluene/n-heptane as eluent. The eluate was purified by recrystallization from a CH₂Cl₂/acetone mixed solvent to give 15.7 g (yield: 65.0%) of Compound 1-2 as white powder.

The white powder was analyzed by NMR analysis to identify the structure. As a result, the following 48 signals of hydrogen were observed in ¹H-NMR (DMSO-d₆). δ (ppm)=7.65 (4H), 7.49-7.18 (24H), 6.86-6.78 (8H), and 1.29 (12H)

Example 2—Compound 2-1 Synthesis of 2,2′-bis[di-(4-biphenyl)amino]biphenyl

In a reaction vessel purged with nitrogen were put 13.9 g of bis(4-biphenyl)amine, 8.0 g of 2,2′-diiodobiphenyl, 0.1 g of copper powder, 6.8 g of potassium carbonate, and 10 ml of dodecylbenzene. The mixture was stirred under reflux for 72 hours, the reaction mixture cooled, toluene added for extraction to remove insoluble matter, the extract filtered, and the filtrate concentrated. The concentrate was purified by recrystallization from a toluene/acetone mixed solvent to yield 10.9 g (70.0%) of Compound 2-1 as white powder.

The structure of the resulting white powder was identified by NMR analysis. As a result, the following 44 signals of hydrogen were detected in ¹H-NMR (DMSO-d₆). δ (ppm)=7.50 (8H), 7.39-7.30 (14H), 7.28-7.25 (10H), 6.96 (4H), and 6.76 (8H).

Example 3—Compound 2-4 Synthesis of 2,2′-bis[biphenyl-4-yl-(9,9-dimethyl-9H-fluoren-2-yl)amino]biphenyl

In a reaction vessel purged with nitrogen were put 15.7 g of biphenyl-4-yl(9,9-dimethyl-9H-fluoren-2-yl)amine, 8.0 g of 2,2′-diiodobiphenyl, 0.1 g of copper powder, 6.8 g of potassium carbonate, and 10 ml of dodecylbenzene. The mixture was stirred under reflux for one week, the reaction mixture cooled, toluene added for extraction to remove insoluble matter, the extract filtered, and the filtrate concentrated. The concentrate was purified by recrystallization from acetone to yield 12.7 g (73.8%) of Compound 2-4 as white powder.

The structure of the resulting white powder was identified by NMR analysis. As a result, the following 52 signals of hydrogen were detected in ¹H-NMR (DMSO-d₆). δ (ppm)=7.66 (2H), 7.57 (2H), 7.48-7.14 (24H), 7.02 (2H), 6.83-6.64 (10H), 1.29 (6H), and 1.02 (6H).

The melting temperature and glass transition temperature of the compounds prepared in Examples were determined using a high-sensitivity differential scanning calorimeter (DSC 3100SA, from Bruker AXS).

Melting Glass Transition Temp. (° C.) Temperature (° C.) Compound 1-2 (Example 1) ND 126 Compound 2-1 (Example 2) 248 123 Compound 2-4 (Example 3) ND 146

It is seen that the aryldiamine compounds of the invention have a glass transition temperature of 100° C. or higher and are therefore stable in thin film form.

A 100 nm thick film was deposited on an ITO substrate by evaporation of each of the compounds obtained in Examples. The work function of the film was determined using an ionization potential measuring device (PYS-202, available from Sumitomo Heavy Industries, Ltd.).

Work Function (eV) Compound 1-2 of Example 1 5.62 Compound 2-1 of Example 2 5.71 Compound 2-4 of Example 3 5.69

It is seen that the aryldiamine compounds of the invention exhibit suitable energy levels as compared with commonly used hole transporting materials with a work function of 5.4 eV, such as NPD and TPD, and therefore have good hole transporting ability.

Device Example 1

A glass substrate 1 having an ITO electrode as a transparent anode 2 formed thereon beforehand was provided. A hole injection layer 3, a first hole transport layer 4, a second hole transport layer 5, an emitting layer 6, an electron transport layer 7, an electron injection layer 8, and a cathode 9 (aluminum electrode) were evaporation-deposited on the ITO substrate in the order described in FIG. 4 to make an organic EL device.

More specifically, a glass substrate 1 with a 150 nm-thick ITO layer was cleaned with isopropyl alcohol under ultrasonication for 20 minutes. After drying on a hot plate heated to 200° C. for 10 minutes, the ITO glass substrate was further cleaned by UV/ozone for 15 minutes. The thus cleaned ITO glass substrate was set in a vacuum deposition chamber, and the chamber was evacuated to 0.001 Pa or lower.

Compound HIM-1 shown below was evaporation-deposited to cove the transparent anode 2 to form a 5 nm thick hole injection layer 3.

On the hole injection layer 3 was evaporation-deposited a triphenylamine derivative HTM-1 shown below to form a 60 nm thick first hole transport layer 4.

On the first hole transport layer 4 was evaporation-deposited Compound 1-2 of Example 1 to form a 5 nm thick second hole transport layer 5.

On the second hole transport layer 5 were co-deposited an iridium complex EMD-1 shown below and a carbazole derivative EMH-1 below at an EMD-1:ETH-1 deposition rate ratio of 5:95 to form a 20 nm thick emitting layer 6.

On the emitting layer 6 were co-deposited a pyrimidine compound ETM-1 below and a compound ETM-2 below at an ETM-1:ETM-2 deposition rate ratio of 50:50 to form a 30 nm thick electron transport layer 7.

Lithium fluoride was evaporation-deposited on the electron transport layer 7 to form a 1 nm thick electron injection layer 8.

Finally, aluminum was deposited on the electron injection layer 8 to form a 100 nm thick cathode 9.

Device Example 2

An organic EL device was fabricated in the same manner as in Device Example 1, except that the second hole transport layer 5 was formed using Compound 2-1 of Example 2 in place of Compound 1-2 of Example 1.

Device Example 3

An organic EL device was fabricated in the same manner as in Device Example 1, except that the second hole transport layer 5 was formed using Compound 2-4 of Example 3 in place of Compound 1-2 of Example 1.

Comparative Device Example 1

For comparison, an organic EL device was fabricated in the same manner as in Device Example 1, except that the second hole transport layer 5 was formed using HTM-2 shown below in place of Compound 1-2 of Example 1.

Comparative Device Example 2

For comparison, an organic EL device was fabricated in the same manner as in Device Example 2, except that the second hole transport layer 5 was formed using HTM-3 shown below in place of Compound 2-1 of Example 2.

Comparative Device Example 3

For comparison, an organic EL device was fabricated in the same manner as in Device Example 2, except that the second hole transport layer 5 was formed using HTM-4 shown below in place of Compound 2-1 of Example 2.

Comparative Device Example 4

For comparison, an organic EL device was fabricated in the same manner as in Device Example 2, except that the second hole transport layer 5 was formed using HTM-5 shown below in place of Compound 2-1 of Example 2.

The organic EL devices made in Device Examples 1 to 3 and Comparative Device Examples 1 to 4 were evaluated for characteristics in the atmosphere at ambient temperature. Emission characteristics of each device when a direct voltage was applied were determined. The results obtained are shown in Table 1 below.

The life of the organic EL devices made in Device Examples 1 to 3 and Comparative Device Examples 1 to 4 was determined as follows. Each EL device was driven at a constant current that resulted in an initial luminance (the luminance at the onset of light emission) of 9000 cd/m². The time required for the initial luminance to decay to 8550 cd/m² (95% of the initial luminance) was recorded. The results are shown in Table 1.

TABLE 1 Voltage Luminance Emission Power Efficiency Life 2nd Hole (V) (cd/m²) Efficiency (cd/A) (lm/W) (h) Transport Layer (@10 mA/cm²) (@10 mA/cm²) (@10 mA/cm²) (@10 mA/cm²) (95% decay) Device Example 1 Compound 1-2 4.12 7200 72.05 54.95 200 Device Example 2 Compound 2-1 4.30 7769 77.77 56.82 340 Device Example 3 Compound 2-4 4.12 7629 76.41 58.34 337 Comparative Device HTM-2 4.20 6990 69.95 52.33 111 Example 1 Comparative Device HTM-3 4.28 7291 73.00 53.59 216 Example 2 Comparative Device HTM-4 4.20 7065 70.70 52.89 305 Example 3 Comparative Device HTM-5 4.45 7424 74.31 52.47 200 Example 4

Comparing the organic EL devices of Device Example 1 and Comparative Device Example 1, in which the aryldiamine compounds used to form the second hole transport layer 5 were structurally similar except for the phenylene group linking the two amino groups, the emission efficiency of the device of Comparative Device Example 1 was 69.95 cd/A with a current density of 10 mA/cm² applied, whilst that of the device of Device Example 1 was as high as 72.05 cd/A.

The power efficiency of the organic EL device of Comparative Device Example 1 was 52.33 lm/W, whereas that of the device of Device Example 1 was as high as 54.95 lm/W.

The life (95% decay) of the organic EL device of Comparative Device Example 1 was 111 hours, whilst the device of Device Example 1 showed a remarkable extension of life to as long as 200 hours.

Similarly, when comparing the organic EL devices of Device Example 2 and Comparative Device Examples 2 to 4, in which the aryldiamine compounds used to form the second hole transport layer 5 were structurally similar except for the biphenylene group linking the two amino groups, the emission efficiency of the devices of Comparative Device Examples 2 to 4 was between 70.70 cd/A and 74.31 cd/A with a current density of 10 mA/cm² applied, while that of the device of Device Example 2 was as high as 77.77 cd/A.

The power efficiency of the organic EL devices of Comparative Device Examples 2 to 4 was from 52.47 to 53.59 lm/W, whereas that of the device of Device Example 2 was as high as 56.82 lm/W.

The life (95% decay) of the organic EL devices of Comparative Device Examples 2 to 4 was 200 to 305 hours, whereas the device of Device Example 2 showed an extension of life to as long as 340 hours.

Similarly, on comparing the organic EL devices of Device Examples 2 and 3, in which the aryldiamine compounds used to form the second hole transport layer 5 were structurally the same except for Ar² and Ar³ in formula (1), it is seen that the organic EL device of Device Example 2, in which Ar² and Ar³ in formula (1) were each an aromatic hydrocarbon group having a fused polycyclic structure, exhibited a higher emission efficiency and a longer life than that of Device Example 3, in which Ar² and Ar³ in formula (1) were each an aromatic hydrocarbon group having no fused polycyclic structure.

The above results prove that the organic EL device using the aryldiamine compound of the invention achieves a higher emission efficiency and a longer life than conventional organic EL devices.

INDUSTRIAL APPLICABILITY

The aryldiamine compound of the invention exhibits high hole transporting properties and high electron blocking properties and is stable in its thin film form and is therefore excellent as a material for fabricating organic EL devices. The organic EL device of the invention, which is fabricated by using the compound of the invention, exhibits high emission efficiency and high power efficiency, requires a low driving voltage, and shows excellent durability. Therefore, the organic EL device of the invention is promising for application to home appliances and lighting equipment.

REFERENCE SIGNS LIST

-   1: Glass substrate -   2: Transparent anode -   3: Hole injection layer -   4: First hole transport layer -   5: Second hole transport layer -   6: Emitting layer -   7: Electron transport layer -   8: Electron injection layer -   9: Cathode 

1. An aryldiamine compound represented by formula (1):

wherein m and n each represent 0 or 1; Ar¹, Ar², Ar³, and Ar⁴ each represent an aromatic hydrocarbon group or an aromatic heterocyclic group; when m+n is 0 or 1, and Ar² is an unsubstituted phenyl group, neither Ar³ nor Ar⁴ is an unsubstituted phenyl group; L¹ and L² each represent a single bond, a divalent aromatic hydrocarbon group, or a divalent aromatic heterocyclic group; and R¹, R², and R³ each represent a hydrogen atom, a deuterium atom, a fluorine atom, a chlorine atom, a cyano group, a nitro group, an alkyl group having 1 to 6 carbon atoms, a cycloalkyl group having 5 to 10 carbon atoms, an alkenyl group having 2 to 6 carbon atoms, an alkoxy group having 1 to 6 carbon atoms, a cycloalkoxy group having 5 to 10 carbon atoms, an aromatic hydrocarbon group, an aromatic heterocyclic group, or an aryloxy group.
 2. The aryldiamine compound according to claim 1, wherein m and n in formula (1) are both zero, being represented by formula (1-1a):

wherein Ar⁵ and Ar⁸ each represent an aromatic hydrocarbon group or an aromatic heterocyclic group; Ar⁶ and Ar⁷ correspond to Ar² and Ar³ in formula (1), respectively; when Ar⁶ is an unsubstituted phenyl group, Ar⁷ is not an unsubstituted phenyl group; R⁴ corresponds to R³ in formula (1); R⁵⁻⁸ represents multiple groups R⁵, R⁶, R⁷, and R⁸ bonded to the benzene ring at different positions; R⁹⁻¹² represents multiple groups R⁹, R¹⁰, R¹¹, and R¹² bonded to the benzene ring at different positions; and R⁵, R⁶, R⁷, R⁸, R⁹, R¹⁰, R¹¹, and R¹² each represent a hydrogen atom, a deuterium atom, a fluorine atom, a chlorine atom, a cyano group, a nitro group, an alkyl group having 1 to 6 carbon atoms, a cycloalkyl group having 5 to 10 carbon atoms, an alkenyl group having 2 to 6 carbon atoms, an alkoxy group having 1 to 6 carbon atoms, a cycloalkoxy group having 5 to 10 carbon atoms, an aromatic hydrocarbon group, an aromatic heterocyclic group, or an aryloxy group.
 3. The aryldiamine compound according to claim 1, wherein m and n in formula (1) are both zero, being represented by formula (1-1b):

wherein Ar⁹ and Ar¹⁰ correspond to Ar² and Ar³ in formula (1), respectively; when Ar⁹ is an unsubstituted phenyl group, Ar¹⁰ is not an unsubstituted phenyl group; R¹³ corresponds to R³ in formula (1); R¹⁴⁻¹⁸ represents multiple groups R¹⁴, R¹⁵, R¹⁶, R¹⁷, and R¹⁸ bonded to the benzene ring at different positions; R¹⁹⁻²² represents multiple groups R¹⁹, R²⁰, R²¹, and R²² bonded to the benzene ring at different positions; R²³⁻²⁶ represents multiple groups R²³, R²⁴, R²⁵, and R²⁶ bonded to the benzene ring at different positions; R²⁷⁻³¹ represents multiple groups R²⁷, R²⁸, R²⁹, R³⁰, and R³¹ bonded to the benzene ring at different positions; and R¹⁴, R¹⁵, R¹⁶, R¹⁷, R¹⁸, R¹⁹, R²¹, R²², R²³, R²⁴, R²⁵, R²⁶, R²⁷, R²⁸, R²⁹, R³⁰, and R³¹ each represent a hydrogen atom, a deuterium atom, a fluorine atom, a chlorine atom, a cyano group, a nitro group, an alkyl group having 1 to 6 carbon atoms, a cycloalkyl group having 5 to 10 carbon atoms, an alkenyl group having 2 to 6 carbon atoms, an alkoxy group having 1 to 6 carbon atoms, a cycloalkoxy group having 5 to 10 carbon atoms, an aromatic hydrocarbon group, an aromatic heterocyclic group, or an aryloxy group.
 4. The aryldiamine compound according to claim 1, wherein m is 1 and n is 0 in formula (1), being represented by formula (1-2a):

wherein Ar¹¹ and Ar¹⁴ each represent an aromatic hydrocarbon group or an aromatic heterocyclic group; Ar¹² and Ar¹³ correspond to Ar² and Ar³ in formula (1), respectively; when Ar¹² is an unsubstituted phenyl group, Ar¹³ is not an unsubstituted phenyl group; R³² corresponds to R¹ in formula (1); R³³ corresponds to R³ in formula (1); R³⁴⁻³⁷ represents multiple groups R³⁴, R³⁵, R³⁶, and R³⁷ bonded to the benzene ring at different positions; R³⁸⁻⁴¹ represents multiple groups R³⁸, R³⁹, R⁴⁰, and R⁴¹ bonded to the benzene ring at different positions; and R³⁴, R³⁵, R³⁶, R³⁷, R³⁸, R³⁹, R⁴⁰, and R⁴¹ each represent a hydrogen atom, a deuterium atom, a fluorine atom, a chlorine atom, a cyano group, a nitro group, an alkyl group having 1 to 6 carbon atoms, a cycloalkyl group having 5 to 10 carbon atoms, an alkenyl group having 2 to 6 carbon atoms, an alkoxy group having 1 to 6 carbon atoms, a cycloalkoxy group having 5 to 10 carbon atoms, an aromatic hydrocarbon group, an aromatic heterocyclic group, or an aryloxy group.
 5. The aryldiamine compound according to claim 1, wherein m is 1 and n is 0 in formula (1), being represented by formula (1-2b):

wherein Ar¹⁵ and Ar¹⁶ correspond to Ar² and Ar³ in formula (1), respectively; when Ar¹⁵ is an unsubstituted phenyl group, Ar¹⁶ is not an unsubstituted phenyl group; R⁴² corresponds to R¹ in formula (1); R⁴³ corresponds to R³ in formula (1); R⁴⁴⁻⁴⁸ represents multiple groups R⁴⁴, R⁴⁵, R⁴⁶, R⁴⁷, and R⁴⁸ bonded to the benzene ring at different positions; R⁴⁹⁻⁵² represents multiple groups R⁴⁹, R⁵⁰, R⁵¹, and R⁵² bonded to the benzene ring at different positions; R⁵³⁻⁵⁶ represents multiple groups R⁵³, R⁵⁴, R⁵⁵, and R⁵⁶ bonded to the benzene ring at different positions; R⁵⁷⁻⁶¹ represents multiple groups R⁵⁷, R⁵⁸, R⁵⁹, R⁶⁰, and R⁶¹ bonded to the benzene ring at different positions; and R⁴⁴, R⁴⁵, R⁴⁶, R⁴⁷, R⁴⁸, R⁴⁹, R⁵⁰, R⁵¹, R⁵², R⁵³, R⁵⁴, R⁵⁵, R⁵⁶, R⁵⁷, R⁵⁸, R⁵⁹, R⁶⁰, and R⁶¹ each represent a hydrogen atom, a deuterium atom, a fluorine atom, a chlorine atom, a cyano group, a nitro group, an alkyl group having 1 to 6 carbon atoms, a cycloalkyl group having 5 to 10 carbon atoms, an alkenyl group having 2 to 6 carbon atoms, an alkoxy group having 1 to 6 carbon atoms, a cycloalkoxy group having 5 to 10 carbon atoms, an aromatic hydrocarbon group, an aromatic heterocyclic group, or an aryloxy group.
 6. The aryldiamine compound according to claim 1, wherein m and n in formula (1) are both one, being represented by formula (1-3a):

wherein Ar¹⁷ and Ar²⁰ each represent an aromatic hydrocarbon group or an aromatic heterocyclic group; Ar¹⁸ and Ar¹⁹ correspond to Ar² and Ar³ in formula (1), respectively; R⁶² and R⁶³ correspond to R¹ and R² in formula (1), respectively; R⁶⁴ corresponds to R³ in formula (1); R⁶⁵⁻⁶⁸ represents multiple groups R⁶⁵, R⁶⁶, R⁶⁷, and R⁶⁸ bonded to the benzene ring at different positions; R⁶⁹⁻⁷² represent multiple groups R⁶⁹, R⁷⁰, R⁷¹, and R⁷² bonded to the benzene ring at different positions; and R⁶⁵, R⁶⁶, R⁶⁷, R⁶⁸, R⁶⁹, R⁷⁰, R⁷¹, and R⁷² each represent a hydrogen atom, a deuterium atom, a fluorine atom, a chlorine atom, a cyano group, a nitro group, an alkyl group having 1 to 6 carbon atoms, a cycloalkyl group having 5 to 10 carbon atoms, an alkenyl group having 2 to 6 carbon atoms, an alkoxy group having 1 to 6 carbon atoms, a cycloalkoxy group having 5 to 10 carbon atoms, an aromatic hydrocarbon group, an aromatic heterocyclic group, or an aryloxy group.
 7. The aryldiamine compound according to claim 1, wherein m and n in formula (1) are both one, being represented by formula (1-3b):

wherein Ar²¹ and Ar²² correspond to Ar² and Ar³ in formula (1), respectively; R⁷³ and R⁷⁴ correspond to R¹ and R² in formula (1), respectively; R⁷⁵ corresponds to R³ in formula (1); R⁷⁶⁻⁸⁰ represents multiple groups R⁷⁶, R⁷⁷, R⁷⁸, R⁷⁹, and R⁸⁰ bonded to the benzene ring at different positions; R⁸¹⁻⁸⁴ represents multiple groups R⁸¹, R⁸², R⁸³, and R⁸⁴ bonded to the benzene ring at different positions; R⁸⁵⁻⁸⁸ represents multiple groups R⁸⁵, R⁸⁶, R⁸⁷, and R⁸⁸ bonded to the benzene ring at different positions; R⁸⁹⁻⁹³ represents multiple groups R⁸⁹, R⁹⁰, R⁹¹, R⁹², and R⁹³ bonded to the benzene ring at different positions; and R⁷⁶, R⁷⁷, R⁷⁸, R⁷⁹, R⁸⁰, R⁸¹, R⁸², R⁸³, R⁸⁴, R⁸⁵, R⁸⁶, R⁸⁸, R⁸⁹, R⁹⁰, R⁹¹, R⁹², and R⁹³ each represent a hydrogen atom, a deuterium atom, a fluorine atom, a chlorine atom, a cyano group, a nitro group, an alkyl group having 1 to 6 carbon atoms, a cycloalkyl group having 5 to 10 carbon atoms, an alkenyl group having 2 to 6 carbon atoms, an alkoxy group having 1 to 6 carbon atoms, a cycloalkoxy group having 5 to 10 carbon atoms, an aromatic hydrocarbon group, an aromatic heterocyclic group, or an aryloxy group.
 8. An organic electroluminescent device comprising a pair of electrodes and at least one organic layer disposed between the pair of electrodes, wherein the aryldiamine compound according to claim 1 is used as comprising material of the at least one organic layer.
 9. The organic electroluminescent device according to claim 8, wherein the organic layer is a hole transporting layer.
 10. The organic electroluminescent device according to claim 8, wherein the organic layer is an electron blocking layer.
 11. The organic electroluminescent device according to claim 8, wherein the organic layer is a hole injection layer.
 12. The organic electroluminescent device according to claim 8, wherein the organic layer is an emission layer.
 13. The organic electroluminescent device according to claim 9, wherein the hole transporting layer is a dual layer composed of a first hole transport layer and a second hole transport layer. 